SELECTED THERMO-PHYSICAL PROPERTIES OF ZIRCONIA POWDERS BASED ON RARE EARTH ELEMENTS SUCH AS RE2Zr2O7 (RE - Gd, La, Sm, Nd) FOR THERMAL SPRAY COATING OF BARRIER LAYERSAbstract
Paper presents results of investigations of selected thermophysical properties of ceramics powders RE2Zr2O7 (RE - Gd, La, Nd, Sm) type, used for thermal spray coatings. In comparison also standard powder of ZrO2-8%wg. Y2O3 (Y8SZ) was tested. Using laser-flash method thermal conductivity was designated and specific heat cp by differential scanning calorimetry (DSC) was determined. Measuring temperature varried from 25-1500ºC. The samples tested were sintered at 1000ºC. As a results of tests we obtain that thermal conductivity of RE2Zr2O7 powders at 1000ºC is lower than Y8SZ. At temperature 25-750ºC higher thermal conductivity was observed for La2Zr2O7 than for Y8SZ. The highest specific heat has zirconate powder Y8SZ, and the lowest- powder based on samarium zirconate.
Keywords: thermal spray coatings, plasma spraying, specific heat, thermal diffusivity,
Download 780.8 KB >>