XRD phase investigations of steam oxidized Fe and Ni rich Cr alloys

The aim of this work was to summarise XRD investigations performed after the tests carried out in steam oxidation conditions in the temperature range 700‒800°C for 3000 hours. In this work, two solid-solution strengthened alloys; Haynes...

więcej >>

High temperature corrosion of metallic materials in coal fired power plant boilers

The aim of this work was to perform high temperature tests in steam conditions at 700‒800°C for 3000 hours. In this work seven alloys were studied: Cr rich austenitic steels 309S, 310S, HR3C, and two solid-solution strengthened Ni based allo...

więcej >>

Wettability, reactivity and interfaces in the Gd/TiO2 system

High-temperature interaction of liquid Gd in contact with dense, polycrystalline TiO2 substrate, was investigated. Wettability and reactivity tests were carried out at two different temperatures (1362°C and 1412°C) in flowing ga...

więcej >>

Investigation of the interaction between the CuZn38Pb2 matrix and the Fe reinforcement phase during the production of the complex relief MMCs

The present paper is relevant to the investigation of the interaction between the copper alloy metal matrix (CuZn38Pb2) and the reinforcement phase (Fe) during the production of "hybrid" complex relief MMCs. An innovative production method is...

więcej >>

Wetting behavior of Si-13.5B alloy on polycrystalline h-BN-based substrates

In this work, for the first time the results of an experimental evaluation of the high temperature behavior of molten Si-B alloy in contact with refractory materials at temperatures up to 1750°C, under static argon atmosphere (p = 850-900 mbar...

więcej >>

A comparison of various imaging modes in scanning electron microscopy during evaluation of selected Si/refractory sessile drop couples after wettability tests at ultra-high temperature

In this work, FEI SciosTM field emission gun scanning electron microscope (FEG SEM) equipped with a unique combination of analytical and imaging detectors was utilized to examine structure and chemistry of selected Si/refractory couples...

więcej >>

High-temperature interaction of molten vermicular graphite cast iron with Al2O3 substrate

The wetting behavior and reactivity between molten cast iron (originally vermicular graphite cast iron, containing in wt. %: 3.70 C, 2.30 Si, 0.44 Mn, 0.054 P, 0.017 Mg, 0.015 S) and commercial polycrystalline alumina (Al2O3 ...

więcej >>